PRIMACOR™ 5990I

Category:	EAA , Copolymer
Manufacturer:	The Dow Chemical Company
Trademark:	PRIMACOR™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	yKatFu_PRIMACOR-5990I.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Low heat seal temperature, high hot tack

High gloss, excellent clarity

Excellent water, grease and oil resistance

Complies with

U.S. FDA 21 CFR 177.1310(a)(2)

PRIMACOR™ 5990I is an ethylene acrylic acid copolymer with excellent adhesion to metallic, cellulosic, glass and other substrates. In dispersion form, it is a versatile binder for nonwoven fibers, including polypropylene, polyester, glass, nylon and others.

Applications:

Adhesives

Laminations

Foil priming

Heat sealing

Nonwoven binding

Metal/paper coating

Outstanding Properties:

Dispersible in aqueous amines and alkali

"Clean" dispersion requires no salts, surfactants or solvents

Dispersions use existing waterbourne application equipment

High hot tack

Low odor

General Information
Agency Ratings	FDA 21 CFR 177.1310 (a) 2
Forms	Particle
Processing Method	Coating

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.955	g/cm³	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR)			ASTM D1238, ISO 1133
125°C/2.16 kg ¹	65	g/10 min	ASTM D1238, ISO 1133
190°C/2.16 kg ²	1300	g/10 min	ASTM D1238, ISO 1133
Comonomer Content ³	20.0	%	Internal method

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus - 2% Secant (Compression Molded)	22.1	MPa	ASTM D638, ISO 527-2
Tensile Strength (Break, Compression Molded)	6.21	MPa	ASTM D638, ISO 527-2
Tensile Elongation (Break, Compression Molded)	350	%	ASTM D638, ISO 527-2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	40.0	°C	ASTM D1525, ISO 306
Melting Temperature (DSC)	75.0	°C	Internal method

Extrusion instructions
用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。

Note Message
1 .	As measured during production.
2 .	The melt index value is correlated with the melt flow rate (ASTM D 1238 condition is 125°C/2.16kg).
3 .	The comonomer content measured by Dow attribute method has the same accuracy as ASTM D 4094.

Resin Grade	Manufacturer	Category	Trademark
POLYREX® PH-888G	CHI MEI CORPORATION	PS (HIPS)	POLYREX®
RheTech Polypropylene F43-01B	RheTech, Inc.	PP Copolymer	RheTech Polypropylene
Spartech Polycom PP5430	Spartech Polycom	PP, Unspecified	Spartech
Karina WHITE PVC COMPOUND -E TR-652D10/ 1-Y	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Maxxam™ PP5940 B131 C 600R	PolyOne Corporation	PP, Unspecified	Maxxam™