Resilience™ LS11000E
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Resilience™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yIyIVG_ResilienceLS11000E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Resilience™LS11000E is a rigid polyvinyl chloride product,. It can be processed by extrusion and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Resilience™LS11000E application areas include the automotive industry and water pipes/pipes/drinking water. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 16344 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 79 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2480 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 42.1 | MPa | ASTM D638 |
| Flexural Modulus | 2480 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18mm, injection molding | 1100 | J/m | ASTM D256 |
| Transverse flow : 23°C, 3.18mm, molded | 1100 | J/m | ASTM D256A |
| Flow : 23°C, 3.18mm, molded | 1000 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 53.4 | J/cm | ASTM D4226 |
| 23°C 4 | 53.4 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 73.3 | °C | ASTM D648 |
| CLTE - Flow | 6.7E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm, ALL | V-0 | UL 94 | |
| 1.9 mm, ALL | 5VA | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Excellent | ||
| Note: Automotive OEM approval(s.Note: NSF listings are obtained on specific colors. Contact PolyOne for the latest listing of approved colors for this products.Note: The Cell Classification was determined using the notched Izaod test with injection molded samples. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Program A, C.125 Dart |
| 4 . | Program B, C.125 Dart |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2286 HF TFE 15 | RTP Company | PEEK | RTP |
| RTP 601 TFE 10 | RTP Company | ABS | RTP |
| SABIC® LDPE 2102N0W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Taitacell EPS 391T | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Hostacom ERC 2061N | LyondellBasell Industries | PP, Unspecified | Hostacom |