Geon™ Bold L5800
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Bold |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yIoYkV_Geon-Bold-L5800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Custom molding |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 79 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2230 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 31.6 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 55 | % | ASTM D638 |
| Flexural Modulus 4 | 2340 | MPa | ASTM D790 |
| Flexural Strength 5(Yield) | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Compression Molded) | 27 | J/m | ASTM D256 |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 6 | 59.2 | J/cm | ASTM D4226 |
| 23°C 7 | > 178 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 8 | ASTM D648 | ||
| 0.45 MPa, annealed, 3.18mm | 60.7 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 49.9 | °C | ASTM D648 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Physical properties based on Geon Bold L5800 LHB Black 2880. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 149 - 177 | °C |
| Extrusion instructions |
|---|
| Melt flow, extrusion conditions and downstream calibration likely to be different than standard rigid PVC. Wet vacuum calibration is recommended instead of dry calibration. |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Type 1, 5.1 mm/min |
| 4 . | 51 mm/min |
| 5 . | 51 mm/min |
| 6 . | Procedure a, .125" |
| 7 . | Procedure B, .125" |
| 8 . | Conditioned at 50 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 7573 UVH | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| ACCUTECH™ HP0336M30CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Fainplast PVC HGKA 81 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LNP™ LUBRICOMP™ OCP36 compound | SABIC Innovative Plastics | PPS | LNP™ LUBRICOMP™ |
| Sylvin 8887-95 Brown 7400 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |