Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
Manufacturer: | Korea Engineering Plastics Co., Ltd |
Trademark: | Kepital® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | yH1geG_KepitalFG2025K.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
10% glass fiber filled medium viscosity grade good for general injection molding. FG2025K is good for parts requiring moderate stiffness, stregnth, creep resistance, and HDT. |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.48 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) | 13 | g/10 min | ISO 1133 |
Molding Shrinkage - Flow (3.00 mm) | 1.0 - 1.3 | % | ISO 294-4 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress (Break, 23°C) | 110 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
Flexural Modulus (23°C) | 4800 | MPa | ISO 178 |
Flexural Stress (23°C) | 160 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength | 6.5 | kJ/m² | ISO 179/1A |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature (1.8 MPa, Unannealed) | 160 | °C | ISO 75-2/A |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
Flammability | Nominal Value | Unit | Test Method |
---|---|---|---|
Flame Rating | HB | UL 94 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
SABIC® Vestolen A 6060R b | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
TUFNYL® SFM 24 BLACK | SRF Ltd. | Nylon 6 | TUFNYL® |
Aaroprene® GFIPP 2030 | Aaron Industries Corp. | PP, Unspecified | Aaroprene® |
Nymax™ 600 A Zip 43 Natural | PolyOne Corporation | Nylon 6 Alloy | Nymax™ |
AIE PA6 50G6F | Asia International Enterprise (Hong Kong) Limited | Nylon 6 | AIE PA6 |