TEKAFIN™ PB50M20
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAFIN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yH0MIE_TEKAFIN-PB50M20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PB50M20 is MF25% reinforced Compounded-PP. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 32.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 32 | % | ASTM D638 |
| Flexural Modulus 3 | 2270 | MPa | ASTM D790 |
| Flexural Strength 4 | 45.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 41 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 136 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH PZ503 | Polyram Ram-On Industries | PC | RAMTOUGH |
| ALCOM® PC 740/4 UV WT1368-04LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Dynacom 304 | Dynachem Co. Ltd. | Nylon 66 | Dynacom |
| Karina BLACK PVC COMPOUND -E 601D48/ 1-A | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| StarFlex® 7027-1000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |