Vipel® F086-HHH-00
| Category: | Vinyl Ester , Vinyl Ester |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Vipel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yGoRuM_Vipel-F086-HHH-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vipel Corrosion Resistant Epoxy Novolac, Vinyl Ester Resin The Vipel F086 series is an epoxy novolac vinyl ester resin dissolved in styrene and designed for high temperature resistance. The Vipel F086 series is ideally suited for use in hand lay-up, spray-up, and filament winding processes where outstanding mechanical properties and resistance to chemicals, oxidation and heat are required. Corrosion resistance Vipel F086 is designed for high temperature resistance. The epoxy novolac backbone provides resistance to acids and has superior resistance to many organic solvents. Vipel F086 series is generally resistant to liquids and vapors at higher temperatures than standard bisphenol-A epoxy vinyl ester resins or standard novolacs. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. Mechanical Properties The Vipel F086 series is suitable for moldings that are subjected to particularly high temperature applications. Versatile Suitable for various fabricating methods such as hand lay-up, filament winding, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | |
| Styrene Content | 25 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Gel Time 1(82°C) | 12.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Gel to Peak | 5.0 | min | |
| Peak Exotherm | 186 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 41 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3790 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.8 | % | ASTM D638 |
| Flexural Modulus | 4210 | MPa | ASTM D790 |
| Flexural Strength | 155 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 166 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity 2(25°C) | 2800 | cP |
| Note Message | |
|---|---|
| 1 . | Gel time with 0.25% Cobalt 6%, 0.05% DMA and 1.25% MEKP |
| 2 . | Brookfield RV viscosity spindle #3 AT 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 9712 | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| Tenogel® ABS A3 HL PRTA011 AB316 | Petropol Industry and Trade of Polymers LTDA | ABS | Tenogel® ABS |
| EOS PA 2200 Top Speed 1.0 | EOS GmbH | Nylon 12 | EOS |
| Hipolyene GM BP 11 | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Sylvin 9077-85 Grey 9398 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |