ELIX™ Ultra 4115
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | ELIX Polymers, S. L. |
| Trademark: | ELIX™ Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yGY3sp_ELIX-Ultra-4115.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELIX Ultra 4115 Very high heat grade with high impact resistance, PC-modified ISO Shortname: ISO 2580-1 -ABS 2-X, MG, 115-04-35-20 |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Part Marking Code (ISO 2580) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (25°C) | 1.08 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow | 0.60 to 0.80 | % | |
| Flow | 0.60 to 0.80 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 100 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2250 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 47.0 | MPa | |
| Break, 23°C | 40.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 3.8 | % | |
| Break, 23°C | 35 | % | |
| Nominal Tensile Strain at Break (23°C) | 20 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 42 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 114 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 102 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 116 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 8.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.00 | ||
| 23°C, 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 4.4E-3 | ||
| 23°C, 1 MHz | 8.4E-3 | ||
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4(2.00 mm) | 32 | mm/min | ISO 3795 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 700 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 70.0 | °C | |
| Injection Velocity | 240 | mm/sec | ISO 294 |
| Note Message | |
|---|---|
| 1 . | 150x105x3 |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | US - FMVSS |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resblend PP/PA | Polimarky Spolka Jawna | Nylon+PP | Resblend |
| RTP 100 FR LF | RTP Company | PP, Unspecified | RTP |
| CarmelStat™ CS 6015 | Carmel Olefins Ltd. | PP, Unspecified | CarmelStat™ |
| Infino HN-3104 | SAMSUNG SDI CO., LTD. | PC | Infino |
| LUVOCOM® 1105-7794/BL VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |