SD POLYCA™ SI8001H
| Category: | PC , Polycarbonate |
| Manufacturer: | Sumika Styron Polycarbonate Limited |
| Trademark: | SD POLYCA™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yGKoQC_SDPOLYCASI8001H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SD POLYCA™ 870 series, SI8001H and SI6001W are based on silicone type flame retardants instead of conventional bromine type and phosphonate type flame retardants. SD POLYCA 870 series, SI8001H and SI6001W are environmentally friendly polycarbonate resins and show excellent hydrolysis resistance, thermal stability, heat resistance and molding capability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 80 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 126 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE B5411 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Toyolac® 440Y MH5 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| UMG ALLOY® CV201 | UMG ABS, Ltd. | PC+ABS | UMG ALLOY® |
| Alpha PVC 3019-40/45 CLEAR 0003 | AlphaGary | PVC, Flexible | Alpha PVC |
| Hanwha Total PE 531G | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LDPE | Hanwha Total PE |