Braskem PE TS7003
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yGIfXM_Braskem-PE-TS7003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TS7003 is a low density polyethylene (LDPE) with high molecular weight that offers high mechanical strength and toughness even at low temperatures. Additionally, this product is easily processed .The product was developed to meet the requirements for automatic packaging. The additive package provides thermal stability during the extrusion, low coefficient of friction - COF, allowing high productivity on the packaging lines. This product is identified as PE 115 according to ASTM D-4976-04a standard specification. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.27 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 50 µm, Blown Film | 140 | MPa | |
| 2% Secant, TD : 50 µm, Blown Film | 150 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 30.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 25.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 370 | % | |
| TD : Break, 50 µm, Blown Film | 680 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 190 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, Blown Film | 300 | g | |
| TD : 50 µm, Blown Film | 220 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 50.0 µm, Blown Film) | 70 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 13 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 205 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKASTER™ F615G30 | Mando Advanced Materials Co., Ltd. | PET | TEKASTER™ |
| Bergadur™ PB40 CF30 U BK003 | PolyOne Corporation | PBT | Bergadur™ |
| Chemraz 655 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Cheng Yu 3265 | Cheng Yu Plastic Company Limited | TPE | Cheng Yu |
| ISOTHANE® 2090A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |