NORYL™ RN0612 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yGA5iG_NORYL-RN0612-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL RN0612 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 30% PCR styrenic series resin content. Designed for good dimensional stability and high flow, this resin also uses non-chlorinated, non-brominated FR additives with a specific density of 1.1 g/cm^3. NORYL RN0612 may be an excellent material candidate for flat panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance and low density. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 280°C/1.2 kg | 13.0 | cm³/10min | |
| 280°C/2.16 kg | 34.0 | cm³/10min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2100 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 43.0 | MPa | ASTM D638 |
| Yield | 42.0 | MPa | ISO 527-2/50 |
| Break 3 | 43.0 | MPa | ASTM D638 |
| Break | 42.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 1.0 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/50 |
| Break 5 | 15 | % | ASTM D638 |
| Break | 18 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 65.0 | MPa | ASTM D790 |
| -- 7 | 2100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 64.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 2100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 41 | J/m | ASTM D256 |
| 23°C | 52 | J/m | ASTM D256 |
| -30°C 10 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 90.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 88.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 78.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 74.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ASTM D1525, ISO 306/B50 10 14 |
| -- | 98.0 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.6E-5 | cm/cm/°C | |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Constant | |||
| 1 MHz | 2.76 | ASTM D150 | |
| 1 MHz | 2.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 3.5E-3 | ASTM D150, IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 725 | °C | |
| 2.00 mm | 725 | °C | |
| 3.00 mm | 725 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Hopper Temperature | 65.0 to 85.0 | °C | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 260 to 295 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Processing (Melt) Temp | 260 to 295 | °C | |
| Mold Temperature | 45.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| 14 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titanvene™ HD5740UA | PT. TITAN Petrokimia Nusantara | HDPE | Titanvene™ |
| Vydyne® 21SPG1 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ULTEM™ CRS5301 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Daelim Po1y® PH-780B | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| Hax™ HF 4221 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |