LNP™ LUBRICOMP™ RBL36L compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yFbC3I_LNP-LUBRICOMP-RBL36L-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RBL36L is a compound based on Nylon 66 containing 30% Glass Bead, 15% PTFE. Added features s of this grade are: Low Extractable, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RBL-4036 LE Product reorder name: RBL36L |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.53 | g/cm³ | ASTM D792 |
| -- | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.43 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.54 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4180 | MPa | ASTM D638 |
| -- | 4100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 66.0 | MPa | ASTM D638 |
| Break | 58.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 8.8 | % | ASTM D638 |
| Break 4 | 9.1 | % | ASTM D638 |
| Break | 8.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 3950 | MPa | ASTM D790 |
| -- 6 | 3820 | MPa | ISO 178 |
| Flexural Stress | 109 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.57 | ||
| vs. Itself - Static | 0.58 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.200 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 32.5 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 41 | J/m | ASTM D256 |
| 23°C 7 | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 340 | J/m | ASTM D4812 |
| 23°C 8 | 23 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.30 | J | ASTM D3763 |
| -- | 1.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 231 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 223 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 91.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 97.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.0E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3865B | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Prime Polypro™ J-721GR | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| NANCAR® 1053X26 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| DIOSHY® TPU T995NC | DIOSHY Co.,Ltd. | TPU-Polyester | DIOSHY® |
| FLEXITEQ™ F60A571 | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |