LNP™ LUBRICOMP™ QCP36 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yFOgwB_LNPLUBRICOMPQCP36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP QCP36 is a compound based on Nylon 6/10 resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Internally Lubricated, , Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound QCL-4536 Product reorder name: QCP36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.80 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.35 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 19900 | MPa | ASTM D638 |
| -- | 19200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 174 | MPa | ASTM D638 |
| Yield | 188 | MPa | ISO 527-2 |
| Fracture | 174 | MPa | ASTM D638 |
| Fracture | 188 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.0 | % | ASTM D638 |
| Yield | 1.9 | % | ISO 527-2 |
| Fracture | 2.0 | % | ASTM D638 |
| Fracture | 6.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 16500 | MPa | ASTM D790 |
| -- | 17000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 283 | MPa | ASTM D790 |
| -- | 289 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.46 | ASTM D3702 Modified | |
| With Self-Static | 0.46 | ASTM D3702 Modified | |
| Wear Factor - Washer | 15.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 7.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 800 | J/m | ASTM D4812 |
| 23°C 3 | 50 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.30 | J | ASTM D3763 |
| -- | 3.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 221 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 222 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 213 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 212 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUCOMP™ CP0400L | ACLO Compounders Inc. | PP Copolymer | ACCUCOMP™ |
| Alkatuff® LL705UV | Qenos Pty Ltd | LLDPE | Alkatuff® |
| Cheng Yu C660F | Cheng Yu Plastic Company Limited | PC+ABS | Cheng Yu |
| Sylvin 5132-86 Clear Blue 8372 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Taizhou Plastic PA-A5-3 | Taizhou Plastic Co., Ltd. | Nylon 6 | Taizhou Plastic |