Elastollan® WY1158
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yEowVr_Elastollan-WY1158.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® WY1158 exhibits excellent toughness, high and low temperature properties, hydrolytic stability and burst pressures for hose and tube applications. Elastollan® WY1158 is supplied uncolored in pellet form. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 94 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 55.8 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 61.4 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 130 | mg | ASTM D1044 |
| Abrasion - DIN | 70 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 107 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 13.8 | MPa | |
| 300% Strain | 19.3 | MPa | |
| Tensile Strength | 27.6 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 480 | % | ASTM D412 |
| Tear Strength 1 | 117 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 10 | % | |
| 70°C, 22 hr | 45 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -41.0 | °C | Internal Method |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 190 to 220 | °C | |
| Front Temperature | 190 to 220 | °C | |
| Nozzle Temperature | 210 to 225 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 170 to 210 | °C | |
| Cylinder Zone 3 Temp. | 170 to 210 | °C | |
| Cylinder Zone 5 Temp. | 170 to 210 | °C | |
| Adapter Temperature | 200 to 220 | °C | |
| Die Temperature | 195 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT REGRIND POMC GC25-100RG | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REGRIND |
| Formolene® LH6008 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| Electrafil® HIPS E | Techmer Engineered Solutions | PS (HIPS) | Electrafil® |
| LNP™ LUBRICOMP™ RFL369 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| MAJORIS BC218 | AD majoris | PP, Unspecified | MAJORIS |