Category: | PPS , Polyphenylene Sulfide |
Manufacturer: | Bada AG |
Trademark: | Badatron® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | yCvm76_BadatronPPSGF30TFSIM15.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
30% glasfibres filled tribological injection moulding grade; Low friction and wear at high high service temperature |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density (23°C) | 1.62 | g/cm³ | ISO 1183 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus (23°C) | 11500 | MPa | ISO 527-2/1 |
Tensile Stress (Break, 23°C) | 160 | MPa | ISO 527-2/5 |
Tensile Strain (Break, 23°C) | 1.7 | % | ISO 527-2/5 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength 1(23°C) | 7.0 | kJ/m² | ISO 179/1eA |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature 2(1.8 MPa, Unannealed, 4.00 mm) | 270 | °C | ISO 75-2/A |
Melting Temperature (DSC) 3 | 295 | °C | ISO 3146 |
Flammability | Nominal Value | Unit | Test Method |
---|---|---|---|
Flame Rating | UL 94 | ||
0.8 mm | V-0 | UL 94 | |
1.6 mm | V-0 | UL 94 | |
Glow Wire Flammability Index | IEC 60695-2-12 | ||
0.75 mm | 960 | °C | IEC 60695-2-12 |
1.6 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
0.75 mm | 960 | °C | IEC 60695-2-13 |
1.6 mm | 960 | °C | IEC 60695-2-13 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 140 | °C | |
Drying Time | 3.0 - 4.0 | hr | |
Processing (Melt) Temp | 300 - 340 | °C | |
Mold Temperature | 140 - 180 | °C |
Note Message | |
---|---|
1 . | 80x10x4 mm |
2 . | 110x10x4 mm |
3 . | Compound for molding, 10k/min |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
RTP 4402 | RTP Company | Nylon, Unspecified | RTP |
SHIN-A SE-55F | SHIN-A T&C | Epoxy | SHIN-A |
Softell CA 02 A | LyondellBasell Industries | Polyolefin, Unspecified | Softell |
SUSTAMID 46 | Röchling Sustaplast SE & Co. KG | Nylon 46 | SUSTAMID |
Latimass 82-02 D030 | LATI S.p.A. | Nylon 12 | Latimass |