Petrothene® NA205000
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yC2MBp_Petrothene-NA205000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene NA205000 is an extrusion coating resin especially recommended for high-speed, light weight coating applications. The resin can be drawn to a low coating weight at line speeds in excess of 1,500 fpm with minimum neck-in and no edge weave. It is recommended for flexible pouches, locker wraps, sugar pouches, industrial and multi-wall bags and laminations. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 56 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 10.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 640 | % | ASTM D638 |
| Flexural Strength | 212 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 329 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV |
| 2 . | Type IV |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VR VRGR 903 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| Nipoflex® 633 | TOSOH Corporation | EVA | Nipoflex® |
| Fainplast PVC PK 96 | Fainplast Compounds S.r.l | PVC, Semi-Rigid | Fainplast PVC |
| ELASTOSIL® AUX MOULD RELEASE AGENT 32 | Wacker Chemie AG | Silicone | ELASTOSIL® AUX |
| KEBATRON® PPS C1065X1 | BARLOG plastics GmbH | PPS | KEBATRON® |