ICORENE® N4420
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ICO Polymers EMEA, A Division of A. Schulman |
| Trademark: | ICORENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yBw9uz_ICORENE-N4420.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ICORENE® N4420 is a polypropylene homopolymer with a high fluidity. It is suitable for injection moulding and its main applications are thin walled packaging items or housewares. ICORENE® N4420 is supplied in powder form and used in masterbatch formulations |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 9.0 | % | ASTM D638 |
| Flexural Modulus | 1250 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 79.0 | °C | ISO 75-2/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 19HT20-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| BESTNYL SI00VI02BU | Triesa Plastics | Nylon 6 | BESTNYL |
| Evoprene™ GC 5654 | AlphaGary | SEBS | Evoprene™ GC |
| Sylvin 2963-70 Blue 8377 | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |
| LNP™ KONDUIT™ PX11311 compound | SABIC Innovative Plastics Asia Pacific | Nylon 6 | LNP™ KONDUIT™ |