LNP™ STAT-KON™ MD000ISC compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yBIuuW_LNPSTATKONMD000ISCcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* MD000ISC is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound M-1 HI Product reorder name: MD000ISC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.6 - 1.8 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.6 - 1.8 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.6 - 1.8 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.6 - 1.8 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 483 | MPa | ASTM D638 |
| -- | 1100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 21.8 | MPa | ASTM D638 |
| Yield | 18.5 | MPa | ISO 527-2 |
| Fracture | 17.1 | MPa | ASTM D638 |
| Fracture | 17.4 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 9.0 | % | ASTM D638 |
| Fracture | 130 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 1140 | MPa | ASTM D790 |
| -- | 1200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 27.5 | MPa | ASTM D790 |
| -- | 27.4 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 830 | J/m | ASTM D256 |
| 23°C 2 | 66 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 3 | 110 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 24.4 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 81.1 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 52.8 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 56.0 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 216 - 227 | °C | |
| Front Temperature | 238 - 249 | °C | |
| Processing (Melt) Temp | 227 - 249 | °C | |
| Mold Temperature | 32.2 - 48.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® P PR0 | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| ARMAMID® PA SVMN 35-1 | Poly Plastic | Nylon 6 | ARMAMID® |
| Fainplast PVC GK 91 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Kumho EPS GN16 | Korea Kumho Petrochemical Co., Ltd. | PS (EPS) | Kumho EPS |
| Sylvin 4200-88 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |