Braskem PE SBF0323/12HC
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem America Inc. |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yAEziK_Braskem-PE-SBF0323-12HC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: SBF0323/12HC is a high molecular weight LDPE produced under high pressure technology. Films obtained with this product show outstanding optical properties, excellent mechanical properties, and good shrinkage. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Additive: Slip Medium. Antiblock Medium. Applications: Automatic packaging of solid and liquid products; shrink films for pallets. Process: Blown Film Extrusion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.32 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 40.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 390 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 1000 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm, Blown Film) | 100 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD (38 µm, Blown Film) | 100 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60 °, blown film) | 83 | ASTM D2457 | |
| Haze (Blown Film) | 11 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 95 | % | ASTM D6866 |
| Blown Film Properties: 38µm thickness film, processed in a 75 mm screw diameter extruder with blow up ratio of 2:1, die gap 1.0 mmRecommended process conditions:Blown Film ExtrusionExtruder:Screw- relation L/D..........16 to 30:1Compression Ratio.........3 to 4:1Screw Package (Mesh)...40/60/40Temperature Profile: 1st zone............................110°C Extruder..........................180°C Die..................................190°C Blow up ratio...................from 2 to 3:1Frostline Height...............maximum equivalent to bubble diameter |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 121-80M300 | ExxonMobil Chemical | TPV | Santoprene™ |
| Shandong PP PG8101 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| NYLEM® 6 HV | EMAS Plastik San.Tic.AS. | Nylon 6 | NYLEM® |
| KW Plastics KWR101-150 | KW Plastics | HDPE | KW Plastics |
| LNP™ STAT-KON™ DX05301C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |