GAPEX® RPP30EA18BK
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yABNsm_GAPEX-RPP30EA18BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Primary use is for battery tray supports. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 4.0 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 3.8 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 72.4 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 5170 | MPa | ASTM D790 |
| -- | 4900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 48 | J/m | ASTM D256 |
| 23°C | 65 | J/m | ASTM D256 |
| -40°C | 4.8 | kJ/m² | ISO 180 |
| 23°C | 6.8 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D256 |
| Dart Drop Impact | 0.565 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 163 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 152 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 139 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Filler Content, ISO 3451/1: 30.2%Tensile Change, ISO 188, 1000 hrs, 140°C: +12%Izod Change, ISO 188, 1000 hrs, 140°C: +12/-5% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 221 - 238 | °C | |
| Middle Temperature | 227 - 243 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Nozzle Temperature | 232 - 260 | °C | |
| Processing (Melt) Temp | 221 - 238 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 5.08 - 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® A60B02 | Polyram Ram-On Industries | Nylon 66 | Polytron® |
| Sindustris PP HI5303A | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Sylvin 9728-45 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Next Nylon 66 Prime Series PGHS33-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| NORYL™ HS2000X resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |