EL-Pro™ P740J
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Pro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y9MWk3_EL-Pro-P740J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Pro P740J is an impact copolymer polypropylene resin suitable for injection molding process. This resin is recommended for product that requires high stiffness and high processibility. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 27 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 2.00mm | 1.4 | % | ASTM D955 |
| Transverse flow : 2.00mm | 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength - Across Flow 1 | ASTM D638 | ||
| Yield | 28.4 | MPa | ASTM D638 |
| Fracture | 19.6 | MPa | ASTM D638 |
| Flexural Modulus | 1230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 29 | J/m | ASTM D256 |
| 0°C | 39 | J/m | ASTM D256 |
| 23°C | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 55.0 | °C | ASTM D648 |
| Brittleness Temperature | -20.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 |
| Melting Temperature | 120 - 163 | °C | ASTM D2117 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 25.0 - 70.0 | °C | |
| Injection Rate | Fast | ||
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Injection Pressure: 40 to 80% of max. pressurePacking and Holding Pressure: 30 to 60% of max. pressureBack Pressure: 10% of max. pressure |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 216 V30 NATURAL FA | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Styroflex® PM | INEOS Styrolution Group GmbH | SBC | Styroflex® |
| Synthos EPS® 1325F/PL | Synthos S.A. | PS (EPS) | Synthos EPS® |
| LG EVA EC28005 | LG Chem Ltd. | EVA | LG EVA |
| VALOX™ 364 resin | SABIC Innovative Plastics | PBT | VALOX™ |