Rilsan® HT CESV P010 TL
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® HT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y7i9zf_Rilsan-HT-CESV-P010-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® HT CESV P010 TL is a flexible polyphthalamide produced from a renewable source, typically used to replace metal in tubing for high-temperature automotive, transportation and other demanding technical applications. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 300°C/2.16 kg | 0.500 | cm³/10min | |
| 300°C/5.0 kg | 3.10 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 74 | ||
| Shore D, 15 sec | 64 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 880 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 41.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 130 | % | ISO 527-2 |
| Flexural Modulus | 820 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 14 | kJ/m² | |
| 23°C | 76 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 255 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hoop Stress | |||
| 23°C | 30.0 | MPa | |
| 150°C | 5.00 | MPa | |
| Renewable Carbon Conent | > 45 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Melt Temperature | 270 to 300 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4080U | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RJM SN501G30 | RJM International, Inc. | Nylon 6 | RJM |
| UBESTA 3035 JU5 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| CoREZYN® CORVE8287 | Interplastic Corporation | Vinyl Ester | CoREZYN® |
| Gallonprene® GP640-9001 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |