Gravi-Tech™ GT6000-0023 Black
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Gravi-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y7AmyD_Gravi-Tech-GT6000-0023-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Gravi-Tech™ GT6000-0023 Black is a Polyamide 6 (Nylon 6) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Gravi-Tech™ GT6000-0023 Black include appliances, automotive, consumer goods, engineering/industrial parts and handles. Primary characteristic: non-toxic. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 to 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 5070 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 64.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 4 | 4550 | MPa | ASTM D790 |
| Flexural Strength 5 | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 53 | J/m | ASTM D256A |
| Unnotched Izod Impact (23°C, 3.18 mm, Injection Molded) | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 194 | °C | |
| 1.8 MPa, Unannealed | 100 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 82.2 to 135 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E165DL | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| THERMORUN® QT99ZA | Mitsubishi Chemical Corporation | TPO (POE) | THERMORUN® |
| Torelina® AR10M | Toray Resin Company | PPS | Torelina® |
| Vaycron® XA78399 | INEOS Compounds | TPE | Vaycron® |
| FORMULA P ELAN 5210 M2 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |