Order Products : sales@su-jiao.com
Petrothene® NA340
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y6bXeu_Petrothene-NA340.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE NA 340 is a series of LDPE/EVA copolymer resins designed for quality bags and special film applications that require clarity and excellent impact strength. Typical applications include heavy produce, textile and frozen food packaging. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 4.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 32 µm | 145 | MPa | |
| 1% Secant, TD : 32 µm | 165 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 32 µm | 25.5 | MPa | |
| TD : Break, 32 µm | 21.4 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 32 µm | 340 | % | |
| TD : Break, 32 µm | 500 | % | |
| Dart Drop Impact (32 µm) | 170 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm | 180 | g | |
| TD : 32 µm | 250 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm) | 75 | ASTM D2457 | |
| Haze (31.8 µm) | 4.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 166 to 191 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cellophane™ 600MSC | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Daploy™ WB130HMS | Borealis AG | PP, HMS | Daploy™ |
| Epocast 1622 FST A/B | Huntsman Advanced Materials | Epoxy | Epocast |
| KYOCERA CT4200H | KYOCERA Chemical Corporation | PI, TS | KYOCERA |
| Ultramid® Structure A3WG12 LFX BK23215 | BASF Corporation | Nylon 66 | Ultramid® |