Sarlink® TPE EE-2272N
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y6LXc2_Sarlink-TPE-EE-2272N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE EE-2272N is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Sarlink®The main characteristics of TPE EE-2272N are: sunlight resistance. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore A, 1 second, injection molding | 75 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 72 | ISO 868 | |
| Shore A, 15 seconds, injection molding | 70 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Transverse flow : 100% strain | 2.11 | MPa | ISO 37 |
| Flow : 100% strain | 2.90 | MPa | ISO 37 |
| Tensile Stress 2 | ISO 37 | ||
| Transverse flow : Fracture | 8.70 | MPa | ISO 37 |
| Flow : Fracture | 5.80 | MPa | ISO 37 |
| Tensile Elongation 3 | ISO 37 | ||
| Transverse flow : Fracture | 790 | % | ISO 37 |
| Flow : Fracture | 620 | % | ISO 37 |
| Tear Strength 4 | ISO 34-1 | ||
| Transverse flow | 28 | kN/m | ISO 34-1 |
| Flow | 31 | kN/m | ISO 34-1 |
| Compression Set 5 | ISO 815 | ||
| 23°C, 22 hr | 20 | % | ISO 815 |
| 70°C, 22 hr | 44 | % | ISO 815 |
| 90°C, 70 hr | 64 | % | ISO 815 |
| 125°C, 70 hr | 81 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -4.0 | % | ISO 188 |
| Flow : 110°C, 1008 hr | -5.9 | % | ISO 188 |
| Transverse flow : 100% strain 110°C, 1008 hr | 18 | % | ISO 188 |
| Flow : 100% strain 110°C, 1008 hr | 16 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -2.3 | % | ISO 188 |
| Flow : 125°C, 168 hr | -8.6 | % | ISO 188 |
| Transverse flow : 100% strain 125°C, 168 hr | 11 | % | ISO 188 |
| Flow : 100% strain 125°C, 168 hr | 12 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -1.3 | % | ISO 188 |
| Flow : 110°C, 1008 hr | -5.2 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -2.8 | % | ISO 188 |
| Flow : 125°C, 168 hr | -11 | % | ISO 188 |
| Change in Shore Hardness in Air | ISO 188 | ||
| Support a, 110°C, 1008 hr 8 | 4.9 | ISO 188 | |
| Support a, 110°C, 1008 hr 9 | 5.0 | ISO 188 | |
| Support a, 110°C, 1008 hr 10 | 3.4 | ISO 188 | |
| Support a, 125°C, 168 hr 11 | 3.9 | ISO 188 | |
| Support a, 125°C, 168 hr 12 | 3.6 | ISO 188 | |
| Support a, 125°C, 168 hr 13 | 2.4 | ISO 188 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 277 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 510mm/min |
| 2 . | Type 1, 510mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | B method, right angle specimen (without cut), 510mm/min |
| 5 . | Type a |
| 6 . | Type 1 |
| 7 . | Type 1 |
| 8 . | 5 sec |
| 9 . | 15 sec |
| 10 . | 1 sec |
| 11 . | 15 sec |
| 12 . | 5 sec |
| 13 . | 1 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AMN Noir T6LD | Arkema | Nylon 12 | Rilsamid® |
| Pyramid™ PEEK KD2152 | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| Wellamid® XT1627-BK2 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Dryflex® AM 75A202B | ELASTO | SEBS+SBS | Dryflex® |
| Eltex® TUB131N2010 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |