GELOY™ XP4025 resin
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y4wx52_GELOY-XP4025-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Available in a wide range of colors and is recommended for unpainted exterior applications. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 6.8 | g/10 min | ASTM D1238 |
| 260°C/5.0 kg | 18 | g/10 min | ASTM D1238 |
| 280°C/3.8 kg | 31 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Transverse flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption (24 hr) | 0.24 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 59.3 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/50 |
| Fracture | 44.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 4.1 | % | ISO 527-2/50 |
| Fracture 2 | 25 | % | ASTM D638 |
| Fracture | 64 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 3 | 2590 | MPa | ASTM D790 |
| -- 4 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 75.0 | MPa | ISO 178 |
| Yield, 50.0mm span 5 | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 37 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 64 | J/m | ASTM D256 |
| 23°C | 170 | J/m | ASTM D256 |
| -30°C 7 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 8 | 21 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 33.9 | J | ASTM D3763 |
| 23°C, Total Energy | 39.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 103 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 9 | 107 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 6.40mm | 90.6 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 10 | 93.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 109 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -20 to 150°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -20 to 150°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM C177 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Untextured) | 90 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 - 98.9 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 232 - 249 | °C | |
| Middle Temperature | 238 - 254 | °C | |
| Front Temperature | 243 - 260 | °C | |
| Nozzle Temperature | 238 - 254 | °C | |
| Processing (Melt) Temp | 254 - 271 | °C | |
| Mold Temperature | 54.4 - 71.1 | °C | |
| Back Pressure | 0.345 - 1.03 | MPa | |
| Screw Speed | 30 - 80 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 - 98.9 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 221 - 232 | °C | |
| Cylinder Zone 2 Temp. | 232 - 243 | °C | |
| Cylinder Zone 3 Temp. | 243 - 254 | °C | |
| Cylinder Zone 4 Temp. | 254 - 266 | °C | |
| Adapter Temperature | 254 - 266 | °C | |
| Melt Temperature | 254 - 271 | °C | |
| Die Temperature | 254 - 266 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 8 hrsMinimum Moisture Content: 0.04 %Roll Stack Temp - Bottom: 74 - 91 °CRoll Stack Temp - Middle: 93 - 110 °CRoll Stack Temp - Top: 102 - 118 °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 sp=62mm |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SL254M | INDELPRO, S.A. de C.V. | PP Random Copolymer | Pro-fax |
| SABIC® LDPE PCG00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Qenos PE GF7660 | Qenos Pty Ltd | HDPE, MMW | Qenos PE |
| DuClear® QW 80 AV | Ducor Petrochemicals BV | PP Random Copolymer | DuClear® |
| Iupilon® MB4306R | Mitsubishi Engineering-Plastics Corp | PC+Polyester | Iupilon® |