GAPEX® HT RNP23MU01BK
| Category: | Nylon+PP , Polyamide + PP |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® HT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y3znxR_GAPEX-HT-RNP23MU01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GAPEX®HT RNP23MU01BK is a polyamide + PP (nylon + PP) material, which contains a 24% glass fabric reinforcement. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. GAPEX®The main characteristics of HT RNP23MU01BK are heat resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.4 | % | ISO 294-4 |
| Flow direction | 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 114 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5110 | MPa | ISO 178 |
| Flexural Stress (23°C) | 155 | MPa | ISO 178 |
| Shear Modulus | 987 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -40°C | 8.1 | kJ/m² | ISO 180 |
| 23°C | 9.6 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 256 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 236 | °C | ISO 75-2/A |
| Additional Information |
|---|
| The values shown for Molding Shrinkage were tested in accordance with ISO 2577.The value shown for Shear Modulus was tested in accordance with ASTM D4065.Flammability, ISO 3795: 31 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP212G15V0 | Kolon Plastics, Inc. | PBT | SPESIN® |
| BCC Resins BC 8760 | BCC Products Inc. | TSU | BCC Resins |
| Hostalen ACP 6541A UV | LyondellBasell Industries | HDPE | Hostalen |
| K-vinyl KK-S-FR-A-88 | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| Sylvin 5145-75 Black 261 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |