PTS PCA-3015
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Polymer Technology and Services, LLC |
| Trademark: | PTS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y3cgGg_PTS-PCA-3015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTS PCA-3015 is a Polycarbonate + PBT (PC+PBT) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: impact resistant. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.75 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.17 mm) | 51.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.17 mm) | 150 | % | ASTM D638 |
| Flexural Modulus (3.17 mm) | 1860 | MPa | ASTM D790 |
| Flexural Strength (Yield, 3.17 mm) | 85.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.17 mm) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 116 | °C | |
| 1.8 MPa, Unannealed | 96.0 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 238 to 254 | °C | |
| Front Temperature | 246 to 268 | °C | |
| Nozzle Temperature | 246 to 266 | °C | |
| Processing (Melt) Temp | 243 to 279 | °C | |
| Mold Temperature | 65.6 to 82.2 | °C | |
| Back Pressure | 0.00 to 3.45 | MPa | |
| Screw Speed | 20 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| FORMULA P FIB 3620/L | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Grilon® TSG-35/4 H black 9836 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| INSTRUC FEPGF10 | Infinity LTL Engineered Compounds | FEP | INSTRUC |
| PENTAMID AHT GV30 H MOS non-colored | PENTAC Polymer GmbH | Nylon 46 | PENTAMID AHT |
| Durethan® BKV 140 H2.0 DUS008 900051 | LANXESS GmbH | Nylon 6 | Durethan® |