CYROVU® HP2 is an impact-modified acrylic-based multipolymer for molding applications. Major use is for point-of-purchase displays. Typical applications include display dispenser, brochure card holders, magazine holders and signage. The polymer offers a balance of great appearance and rough and tumble durability coupled with attractive economics. The material has found many uses in the Display Industry when strength and clarity are required. The material can be decorated by a wide variety of techniques including: silk screening, hot stamping, pressure sensitive labels, pad printing and metalizing. The product is readily adaptable to tooling designed for styrene, ABS or polycarbonate. Parts made from CYROVU® HP compound can be solvent bonded, thermal-bonded and ultrasonic or spin-welded. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Apparent Density | 0.65 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium) | < 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2960 | MPa | ASTM D638 |
| Tensile Strength | 62.1 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 8.0 | % | |
| Flexural Modulus | 2830 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 0°C, 6.35 mm | 27 | J/m | |
| 23°C, 6.35 mm | 37 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm) | 82.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 |
| CLTE - Flow (0 to 100°C) | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3200 µm) | 90.0 | % | ASTM D1003 |
| Haze (3200 µm) | 3.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 204 to 246 | °C | |
| Mold Temperature | 43.3 to 65.6 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® 46GB012 | Reliance Industries Limited | HDPE | RELENE® |
| Shuman PP 510 | Shuman Plastics, Inc. | PP Homopolymer | Shuman PP |
| AEI SX-0610:CM601 | AEI Compounds Limited | XLPE | AEI |
| Chiao Fu PBT PBT312G20 BK | Chiao Fu Enterprises Co., Ltd. | PBT | Chiao Fu PBT |
| Ekaloy® 20 E I 6 | Sattler KunststoffWerk GmbH | PC+ABS | Ekaloy® |