CYCOLAC™ MG34LG resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y29l9I_CYCOLAC-MG34LG-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Automotive: Low gloss ABS for unpainted interior applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| -- | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/3.8 kg) | 6.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 24.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.80 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.80 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2140 | MPa | ASTM D638 |
| -- | 2270 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 40.7 | MPa | ASTM D638 |
| Yield | 38.7 | MPa | ISO 527-2/5 |
| Break 3 | 33.1 | MPa | ASTM D638 |
| Break | 31.3 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.0 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2/5 |
| Break 5 | 25 | % | ASTM D638 |
| Break | 26 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2210 | MPa | ASTM D790 |
| -- 7 | 2060 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 62.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 42 | J/m | ASTM D256 |
| 23°C | 250 | J/m | ASTM D256 |
| -30°C 10 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 18 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 35.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 82.2 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 81.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 98.9 | °C | ASTM D1525 13 |
| -- | 97.0 | °C | ISO 306/B50 |
| -- | 101 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Rear Temperature | 199 to 210 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 232 to 243 | °C | |
| Nozzle Temperature | 232 to 274 | °C | |
| Processing (Melt) Temp | 232 to 274 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michimid K4100GF13-03 | API Polymers, Inc. | Nylon 6 | Michimid |
| THERMOLAST® K TC2TPZ (Series: GP/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Gallonprene® GP420-7001 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Elastocon® STK40 | Elastocon TPE Technologies | TPE | Elastocon® |
| Iupilon® EHR3400 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |