PALSAFE® R 37 Datasheet,PC,pal plast GmbH-SHANGHAI SUSHENG

Message
PALSAFE®R 37 is a polycarbonate (PC) product,. It can be processed by injection molding and is available in Europe. PALSAFE®The application areas of R 37 include electrical/electronic applications and electrical appliances. Features include: flame retardant/rated flame high strength high hardness Impact resistance

General Information
Features	High strength Impact resistance, good Good liquidity High hardness
Uses	Electrical/Electronic Applications Electrical appliances
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)	37.0	cm³/10min	ISO 1133
Water Absorption			ISO 62
Saturated, 23°C	0.30	%	ISO 62
Equilibrium, 23°C, 50% RH	0.18	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2200	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	61.0	MPa	ISO 527-2/1A/50
Tensile Strain (Yield, 23°C)	5.5	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break (23°C)	50	%	ISO 527-2/1A/50

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	143	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	275	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	V-2		UL 94

Additional Information
Melt-Volume Flow Rate, ISO 1133, 300°C/1.2 kg: 34 to 40 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2100 to 2300 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 59 to 63 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 5 to 6 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 141 to 144 °CDensity, ISO 1183: 1.18 to 1.2 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.25 to 0.35 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Additional Information

Melt-Volume Flow Rate, ISO 1133, 300°C/1.2 kg: 34 to 40 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2100 to 2300 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 59 to 63 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 5 to 6 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 141 to 144 °CDensity, ISO 1183: 1.18 to 1.2 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.25 to 0.35 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Resin Grade	Manufacturer	Category	Trademark
Ravathane R130A85	RAVAGO Kimya Plastik Sanayi ve Ticaret A.S.	TPU-Polyester	Ravathane
Fainplast PVC KL 01589	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC
FRblend® PP-1501	Colour Image Plastic Compound Sdn. Bhd. (CIPC)	PP, Unspecified	FRblend®
Osterlene® PPH-18-.5	Osterman & Company	PP Homopolymer	Osterlene®
POLYCOMPO PE 50	POLYCOMPO Co.,Ltd.	LDPE	POLYCOMPO PE

Category:	PC , Polycarbonate
Manufacturer:	pal plast GmbH
Trademark:	PALSAFE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	y1ZMeP_PALSAFE-R-37.pdf
PRICE:	Order Products email sales@su-jiao.com