DE289 is a 20% mineral filled, polypropylene compound, elastomer modified intended for injection moulding. DE289 has been developed especially for applications requiring excellent impact strength good surface quality and a lower coefficient of friction. The product is available in natural and black (DE289 - 8229) but other colours can be provided on request. APPLICATION
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.60 - 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 17.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 1600 | MPa | ISO 178 |
| Flexural Stress | 31.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 57.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCLAIR® 2710 | NOVA Chemicals | HDPE | SCLAIR® |
| Moplen PPU 1752HL23 | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| 4MID® 9A22150 FRR1 | 4Plas | Nylon 66 | 4MID® |
| Karina IVORY PVC COMPOUND -E 700-35/1-EX | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Daelim Po1y® XP9400 | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |