Flexirene® FF 25
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Flexirene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y0IfiC_Flexirene-FF-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flexirene FF 25 is a LLDPE with butene copolymer, with antioxidants, suitable for blown film extrusion. Flexirene FF 25 is characterised by a high elongational viscosity leading to a good bubble stability during extrusion. Main Application Flexirene FF 25 U is recommended for the production of agricultural film, heavy duty bags, in blend or coextrusion with LDPE. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 15 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 200 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 210 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 11.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 45.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 32.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 580 | % | |
| TD : Break, 25 µm, Blown Film | 800 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 100 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 25.0 | kN/m | |
| TD : 25.0 µm | 180.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 98.0 | °C | ISO 306/A |
| Melting Temperature | 120 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 12 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP732 | Southern Polymer, Inc. | HDPE | PRIMALENE |
| RAYPRENE® NB221-S4088 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| EcoPaXX® Q-X07209 | DSM Engineering Plastics | Nylon 410 | EcoPaXX® |
| Kumho PPG 3601 | Korea Kumho Petrochemical Co., Ltd. | POP | Kumho PPG |
| Marlex® 5626 | Chevron Phillips Chemical Company LLC | LDPE | Marlex® |