PLUSTEK RA325J5
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y0DyKX_PLUSTEK-RA325J5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% GLASS- BEADS AND GLASS-FIBER REINFORCED, FLAME RETARDANT POLYAMIDE 66 FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.60 | % | ASTM D955 |
| -- | 0.50 - 0.60 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 6.0 | % | ASTM D570 |
| Saturated, 23°C | 6.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 75.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3700 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 130 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 40 | J/m | ASTM D256 |
| 23°C | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 80 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.70 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 285 - 310 | °C | |
| Mold Temperature | 65.0 - 110 | °C | |
| Injection Pressure | 70.0 - 125 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 1088 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| THERMOLAST® K TF5CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Hostaform® C 9021 TF5 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Infino HT-8200G | SAMSUNG SDI CO., LTD. | Nylon+PPE | Infino |
| KMI PP KM-047IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |