Ultramid® B35G3 BK00564
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xzvw4h_Ultramid-B35G3-BK00564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B35G3 BK00564 is a 15% glass reinforced, injection molding PA6 grade. Applications Typical applications include internal gas pressure applications such as flashing direction switch gears, automobile mirror housings and wheels of mountain bikes. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.24 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 45.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.6 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 181 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6100 | 3200 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Break, -40°C | 156 | -- | MPa | |
| Break, 23°C | 126 | 67.0 | MPa | |
| Tensile Strain (Break, 23°C) | 2.9 | 13 | % | ISO 527-2 |
| Flexural Stress (23°C) | 189 | 90.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.9 | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 47 | 110 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 214 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 187 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2281 LF TFE 10 | RTP Company | PEEK | RTP |
| SIVIC® 1100 | SIDIAC | NBR | SIVIC® |
| Tufpet PBT G2630 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| AFLAS® 300S | Asahi Glass Co., Ltd. | Fluorelastomer | AFLAS® |
| LNP™ LUBRILOY™ UX98388 compound | SABIC Innovative Plastics | PPA | LNP™ LUBRILOY™ |