Durethan® ECO BKV 20 FN20 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xzKxcc_DurethanECOBKV20FN20000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 20 % glass, injection molding, halogen free flame retardant, contains at least 15 % pre-consumer-recyclate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.31 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 260°C, 2.00mm 1 | 0.80 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.20 | -- | % | ISO 2577 |
| Flow direction : 260°C, 2.00mm 3 | 0.80 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.20 | -- | % | ISO 2577 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 5400 | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 76.0 | 40.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 27 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 5300 | 2300 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | 135 | 50.0 | MPa | ISO 178/A |
| 23°C 6 | 140 | 62.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.8 | 7.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GFHR, 12-050, G20 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Admissible Residence Time at Tmax | min | ||
| Residual Moisture Content | 0.030 - 0.070 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | 75 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 30 | 65 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 155 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | -- | °C | ISO 306/B120 |
| Ball Pressure Test (209°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature 8 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 5.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (23°C, 1.00 mm) | 32 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 0 | -- | UL 746 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | V-2 | -- | UL 94 | |
| 1.50 mm | V-2 | -- | UL 94 | |
| 3.00 mm | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 9 | 30 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPAMID HT 1526 V0 | Vamp Tech | PPA | VAMPAMID |
| NuSil MED-4917 | NuSil Technology | Silicone | NuSil |
| Biffa r-HDPE Tech Grade | Biffa Polymers Ltd | HDPE | Biffa |
| Lumid® GP2130B(W) | LG Chem Ltd. | Nylon 66 | Lumid® |
| Sylvin 9604-85 Green 3198 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |