LEXAN™ 244RF resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xz9XII_LEXAN244RFresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LEXAN 244RF resin grade is a medium viscosity multi purpose product with improved flame resistance and release properties. It is also FDA food contact compliant available in limited colors. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ASTM D792 |
| Specific Volume | 0.830 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C | 0.35 | % | ASTM D570 |
| Equilibrium, 100°C | 0.58 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 70 | ASTM D785 | |
| Class r | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 62.0 | MPa | ASTM D638 |
| Fracture | 68.0 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 130 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 96.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 800 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 3200 | J/m | ASTM D4812 |
| Dart Drop Impact (23°C) | 169 | J | ASTM D3029 |
| Tensile Impact Strength 5 | 577 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 137 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 132 | °C | ASTM D648 |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 6 |
| CLTE - Flow (-40 to 95°C) | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1250 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.27 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Air) | 15 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.17 | ASTM D150 | |
| 60 Hz | 3.17 | ASTM D150 | |
| 1 MHz | 2.96 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 0.010 | ASTM D150 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.0 mm) | 850 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.0 mm) | 875 | °C | IEC 60695-2-13 |
| Oxygen Index | 25 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 271 - 293 | °C | |
| Middle Temperature | 282 - 304 | °C | |
| Front Temperature | 293 - 316 | °C | |
| Nozzle Temperature | 288 - 310 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 71 - 93 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Type S |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa ABS GR-30 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | ABS | Zhongfa |
| ASI POLYETHYLENE LP 552-01 | A. Schulman Inc. | HDPE Copolymer | ASI POLYETHYLENE |
| Hanwha Total PP BI518 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Karina IVORY PVC COMPOUND 105915-35/1-B-IS-EC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TECHNYL® B 218 MX30 NATURAL | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |