Staramide RB006S
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xy1oUO_Staramide-RB006S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide RB006S is a 30% Glass Bead Reinforced Polyamide 66 Injection Molding Resin ( also known as Staramide 66 30K S3) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 1.1 to 1.5 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 5.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 9.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 4400 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 3(23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -40°C | 2.0 | kJ/m² | |
| -20°C | 3.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 235 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 100 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 253 | °C | ISO 306/A50 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 4.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | IEC 60112 | ||
| -- | 500 | V | |
| Solution B | 250 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by E2P) | HB | UL 94 | |
| Oxygen Index | 26 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 260 to 290 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2022TN00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Witcom PA6 2005/43-HF | Witcom Engineering Plastics B.V. | Nylon 6 | Witcom PA6 |
| Geon™ Vinyl Rigid Extrusion L0152 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| LNP™ THERMOCOMP™ DF002ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| Petrothene® M2612GU | LyondellBasell Industries | LDPE | Petrothene® |