VENYL UW300 - 8229
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xx39ZY_VENYL-UW300---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UW300 - 8229 is a 30% glass bead filled polyamide 66 intended for Injection moulding. APPLICATIONS VENYL UW300 - 8229 has been developed especially for very demanding applications in automotive industry and electrical parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.0 to 1.5 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 9.0 | % | ISO 527-2 |
| Flexural Modulus | 3850 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 285 to 300 | °C | |
| Middle Temperature | 280 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 265 to 280 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A1 GF 30 LW | A. Schulman Europe | PBT+PET | SCHULADUR® |
| SLOVAMID® 66 GF 13 TS | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Toyolac® 500 322 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Jiangsu Sinarise EX9125XMU | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Riblene® FF 33 | Versalis S.p.A. | LDPE | Riblene® |