THERMOLAST® V TV7LVZ (Series: LTP)
| Category: | SEPS , Styrene Ethylene Propylene Styrene Block Copolymer |
| Manufacturer: | KRAIBURG TPE |
| Trademark: | THERMOLAST® V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xwZYee_THERMOLAST-V-TV7LVZ-Series-LTP-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The LTP Series is your material solution for sealings requiring high temperature resistance. The compounds are characterized by an excellent adhesion to PP. Typical applications
Material advantages
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 68 | ISO 7619 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Yield) | 6.50 | MPa | ISO 37 |
| Tensile Elongation 2(Break) | 400 | % | ISO 37 |
| Tear Strength 3 | 15 | kN/m | ISO 34-1 |
| Compression Set 4 | ISO 815 | ||
| 23°C, 72 hr | 14 | % | |
| 70°C, 24 hr | 36 | % | |
| 100°C, 24 hr | 37 | % | |
| 120°C, 24 hr | 41 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 220 | °C | |
| Mold Temperature | 25.0 to 40.0 | °C | |
| Injection Pressure | 20.0 to 100 | MPa | |
| Back Pressure | 2.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Type S2, 200 mm/min |
| 2 . | Type S2, 200 mm/min |
| 3 . | Method Bb, Angle (Nicked) |
| 4 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA666G33HS1L-BK10 | Pier One Polymers, Inc. | Nylon 66/6 | MAXAMID™ |
| Rotec® ABS E/S 200 | ROMIRA GmbH | ABS | Rotec® ABS |
| Hostaform® LX90 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Petro Rabigh PP AZ564G | Rabigh Refining & Petrochemical Co. | PP Impact Copolymer | Petro Rabigh PP |
| Ultramid® B3GK24 BK00564 | BASF Corporation | Nylon 6 | Ultramid® |