Celanex® 3400
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xw3EFo_Celanex3400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Celanex 3400 is a general purpose, 40% glass reinforced polybutylene terephthalate that offers a good combination of mechanical, electrical, and thermal properties. This grade provides outstanding processability and good chemical resistance. Celanex 3400 is a high flow material. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow | 0.30 - 0.50 | % | ASTM D955 |
| Transverse flow | 0.70 | % | ISO 294-4 |
| Flow | 0.30 - 0.50 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.12 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 93 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 11700 | MPa | ASTM D638 |
| -- | 12100 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 147 | MPa | ASTM D638 |
| Fracture | 140 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.0 | % | ASTM D638 |
| Fracture | 2.4 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 11000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 215 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.5 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 47 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 223 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 209 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 212 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 45.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3, ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 3 | 19 | kV/mm | ASTM D149 |
| -- | 19 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.90 | ASTM D150 | |
| 100 Hz | 3.50 | IEC 60250 | |
| 1 MHz | 3.40 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 2.0E-3 | ASTM D150 | |
| 1 MHz | 0.013 | IEC 60250 | |
| Arc Resistance | 127 | sec | ASTM D495 |
| Comparative Tracking Index | |||
| -- | 350 | V | IEC 60112 |
| -- | 500 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.71 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20 - 50 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65 - 96 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8202 HS BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| Nypol® PA A3 HL CNZ0263 NR387 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Elastron® D D101.A73.N | Elastron USA, Inc. | SBS | Elastron® D |
| HAIPLEN H10 G4 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| KOCETAL® TC301 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |