Rilsamid® AESN Noir P302 TL
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Arkema |
| Trademark: | Rilsamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xvfNrc_Rilsamid-AESN-Noir-P302-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsamid ® AESN Noir P302 TL is a black coloured polyamide. This grade is plasticized and designed for tube extrusion. AESN Noir P302 TL falls into the PA12-HIPHL category according to DIN 73378. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/5.0 kg) | 18.0 | cm³/10min | ISO 11357 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 71 | ||
| Shore D, 15 sec | 64 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 25.0 | MPa | |
| Break | 54.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 26 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 350 to 450 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 6.00 | mg | ISO 9352 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 173 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA12-HIP, EHL, 22-004 | ISO 1874 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Melt Temperature | 200 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V142-90 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| XANTAR® C CF 407 | Mitsubishi Engineering-Plastics Corp | PC+ABS | XANTAR® C |
| EBAC® SP1802 | Westlake Chemical Corporation | EnBA | EBAC® |
| LNP™ THERMOCOMP™ 9X06482 compound | SABIC Innovative Plastics | Nylon 46 | LNP™ THERMOCOMP™ |
| Sylvin 83032-80UV Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |