SUPRAN® PA3230
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SAMBARK |
| Trademark: | SUPRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xvUkcw_SUPRAN-PA3230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUPRAN® is injection-moldable Long Fiber Reinforced Thermoplastics(LFT), PA3230 is Polyamide reinforced with 30wt% long glass fibers. Parts molded of SUPRAN® have outstanding mechanical properties such as high strength, impact and creep resistance and durability combined with high heat deflection. SUPRAN® PA3230 is suitable for structural parts in industrial application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 121 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.6 | % | ASTM D638 |
| Flexural Modulus | 9810 | MPa | ASTM D790 |
| Flexural Strength | 182 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 460 | J/m | |
| 23°C | 430 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 215 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 260 to 275 | °C | |
| Middle Temperature | 260 to 275 | °C | |
| Front Temperature | 260 to 275 | °C | |
| Mold Temperature | 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 6006CI | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| POLYFLON™ F-201 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| SIBUR Synthetic Rubber NBR 2675 | SIBUR | NBR | SIBUR Synthetic Rubber |
| PENTAMID B GV10 MC20 H2 LS black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| LNP™ LUBRICOMP™ PFL36 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |