Tarnamid® T-27 GF30 V0

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Grupa Azoty S.A.
Trademark:	Tarnamid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	xvAEvo_Tarnamid-T-27-GF30-V0.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Tarnamid®T-27 GF30 V0 is a polyamide 6 (nylon 6) material, and the filler is 30% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding.

Tarnamid®The main features of T-27 GF30 V0 are:

flame retardant/rated flame

chemical resistance

Flame Retardant

Impact modification

high hardness

Typical application areas include:

Automotive Industry

engineering/industrial accessories

safety equipment

packing

Electrical/electronic applications

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	Impact modifier
Features	Impact modification Low friction coefficient Optical Shock absorption Solvent resistance Impact resistance, high Good strength Good wear resistance Good chemical resistance alkali resistance Fatigue resistance Heat resistance, high acid resistance Compliance of Food Exposure High hardness Medium hardness Flame retardancy
Uses	Safety helmet Bar monofilament Engineering accessories Pipe fittings Machine/mechanical parts Furniture Household goods Connector Parts under the hood of a car Automotive Electronics Car interior parts Automotive exterior parts Food packaging Sporting goods Profile Reinforced panel
Forms	Particle
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.64	--	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (275°C/5.0 kg)	40	--	g/10 min	ISO 1133
Molding Shrinkage	0.20	1.4	%	ISO 294-4
Water Absorption (23°C, 24 hr)	0.50	--	%	ISO 62

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness (H 358/30)	240	--	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	10000	--	MPa	ISO 527-2
Tensile Stress (Yield)	160	--	MPa	ISO 527-2
Tensile Strain (Break)	3.0	--	%	ISO 527-2
Flexural Modulus	9000	--	MPa	ISO 178
Flexural Stress (3.5% Strain)	230	--	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength	12	--	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength	60	--	kJ/m²	ISO 179/1eU
Notched Izod Impact	14	--	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	210	--	°C	ISO 75-2/A
Vicat Softening Temperature	210	--	°C	ISO 306/B50

Flammability	Dry	Conditioned		Test Method
Flame Rating (3.20 mm)	V-0	--		UL 94

Additional Information
干燥 Glow Wire Resistance, PN-EN-60695-2-1, 2mm: 960Note: All electrical properties were tested in accordance with the IEC test standard.

Injection	Dry	Unit
Drying Temperature	80.0 - 100	°C
Drying Time	2.0 - 4.0	hr
Suggested Max Moisture	0.20	%
Processing (Melt) Temp	250 - 290	°C
Mold Temperature	80.0 - 120	°C
Injection Pressure	80.0 - 130	MPa
Injection Rate	Moderate

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X4097	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
Propak® 7021	PolyPacific Pty. Ltd.	PP Homopolymer	Propak®
CALP CL230	Lion Idemitsu Composites Co., Ltd.	Polyolefin, Unspecified	CALP
LOTTMER SE-130AN	Lotte Chemical Corporation	SEBS	LOTTMER
Techsil® TIM11123 (GB)	Techsil Limited	Silicone Rubber, RTV-1	Techsil®