KumhoSunny PC/PBT HCB9310G
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PC/PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xukiI0_KumhoSunny-PC-PBT-HCB9310G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HCB9310G is a 10% glass fiber reforced PC/PBT alloy resin, offering high heat resistance, high mechanical strength and good chemical resistance.HCB9310G is recommended for automobile laggage carrier, household appliance, electrician products, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 18 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 to 0.70 | % | ASTM D955 |
| -- | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 82.0 | MPa | ASTM D638, ISO 527-2/5 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 4000 | MPa | ASTM D790 |
| -- 1 | 4100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 125 | MPa | ASTM D790 |
| -- 2 | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 3.20 mm | 100 | J/m | ASTM D256 |
| 23°C | 9.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 70 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 112 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 3 | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 128 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 240 to 275 | °C | |
| Front Temperature | 240 to 275 | °C | |
| Nozzle Temperature | 245 to 270 | °C | |
| Processing (Melt) Temp | 240 to 275 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 H TFE 15 | RTP Company | Nylon 66 | RTP |
| SILVER® SA-2124 | Guangdong Silver Age Sci & Tech. Co., Ltd | SEBS | SILVER® |
| Bergamid™ B700 G30 H GR255 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Sylvin 8280-65 White 1518 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| 3M™ Dyneon™ PTFE Compound 310192004 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |