KOPLA PC KCP1000F
| Category: | PC , Polycarbonate |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xuO8hZ_KOPLA-PC-KCP1000F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PC KCP1000F is a Polycarbonate (PC) material. It is available in Asia Pacific. Important attributes of KOPLA PC KCP1000F are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.80 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.23 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 68.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 100 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2450 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 96.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 780 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 117 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200D AR 15 TFE 5 | RTP Company | Nylon 612 | RTP |
| Sindustris PP HI5205H | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| TABOND 2005 | SILON s.ro | POP | TABOND |
| Boda BDP-H7802 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Hipolyene 5131 RA | Zylog Plastalloys | TPO (POE) | Hipolyene |