MAJORIS UG600 - 8229
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xuNXXI_MAJORIS-UG600---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS UG600 - 8229 is a special 60% long glass fibre reinforced polyamide 66 intended for Injection moulding. APPLICATIONS MAJORIS UG600 - 8229 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.70 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 to 0.50 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.90 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 22500 | 20900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 240 | 225 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 2.1 | % | ISO 527-2 |
| Flexural Modulus | 19100 | 17600 | MPa | ISO 178 |
| Flexural Stress | 403 | 386 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 21 | 22 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 84 | 85 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 290 to 305 | °C | |
| Middle Temperature | 285 to 300 | °C | |
| Front Temperature | 280 to 295 | °C | |
| Nozzle Temperature | 275 to 280 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 95.0 to 120 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 60.0 to 80.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4MID® 9A24400 | 4Plas | Nylon 66 | 4MID® |
| Elvacite® 2013 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |
| Hanwha Total PP SH51 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Karina CLEAR PVC COMPOUND 75/216-DP-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Rotuba CAB B9024 (5% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |