PRL PC-BR1-(color)-5
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xuKslg_PRL-PC-BR1--color--5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PC-BR1-(color)-5 is a Polycarbonate (PC) product. It can be processed by blow molding or extrusion and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 1.0 to 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 70 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 62.1 | MPa | |
| Break, 3.18 mm | 66.2 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 7.0 | % | |
| Break, 3.18 mm | 120 | % | |
| Flexural Modulus (3.18 mm) | 2310 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 750 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | > 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 135 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 129 | °C | |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 1 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 to 124 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 299 to 321 | °C | |
| Cylinder Zone 2 Temp. | 310 to 332 | °C | |
| Cylinder Zone 3 Temp. | 321 to 343 | °C | |
| Melt Temperature | 316 to 343 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 4001 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| MEGOLON™ S540E | AlphaGary | TP, Unspecified | MEGOLON™ |
| SILVER® ABS 350A | Guangdong Silver Age Sci & Tech. Co., Ltd | ABS+PVC | SILVER® |
| Globalene® PT103 | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |
| LNP™ THERMOCOMP™ IF006 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |