UBE Nylon 5033 B Datasheet,Nylon 66/6,UBE Engineering Plastics, S.A.-SHANGHAI SUSHENG

Message
UBE NYLON 5033 B is a basic, high viscosity Polyamide 6/6.6 grade without any additional modification suitable for a wide field of film and extrusion applications. The grade offers an excellent processability and outstanding properties.

General Information
Features	Workability, good Compliance of Food Exposure Viscosity, High
Uses	Films
Agency Ratings	European food contact, not rated
Forms	Particle
Processing Method	Film extrusion Extrusion

Physical	Nominal Value	Unit	Test Method
Density	1.14	g/cm³	ISO 1183

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With self-dynamics	1.0	ASTM D1894
With Self-Static	1.0	ASTM D1894

Films	Nominal Value	Unit	Test Method
Secant Modulus - MD (Cast Film)	400	MPa	ASTM D882
Tensile Strength - MD			ASTM D882
Yield, extruded film	24.0	MPa	ASTM D882
Fracture, extruded film	110	MPa	ASTM D882
Tensile Elongation - MD (Fracture, Extruded Film)	600	%	ASTM D882

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	196	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	ASTM D257

Optical	Nominal Value	Unit	Test Method
Gardner Gloss	155		ASTM D523
Haze	0.50	%	ASTM D1003

Additional Information
The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Oxygen Permeability, ASTM D3985: 40 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 4.08Extractable Content, JIS K6810: <1.0 wt%Moisture content, JIS K6810, in original packaging: <0.1 wt%Molecular Ratio, PA6/PA6.6: 85/15Water Vapor Permeability, JIS Z0208: 125 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 10.0 NPiercing Elongation, JAS P1019, Cast Film: 15 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <5 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <5 hole/0.04 m²

Additional Information

The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Oxygen Permeability, ASTM D3985: 40 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 4.08Extractable Content, JIS K6810: <1.0 wt%Moisture content, JIS K6810, in original packaging: <0.1 wt%Molecular Ratio, PA6/PA6.6: 85/15Water Vapor Permeability, JIS Z0208: 125 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 10.0 NPiercing Elongation, JAS P1019, Cast Film: 15 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <5 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <5 hole/0.04 m²

Resin Grade	Manufacturer	Category	Trademark
Siloxane Masterbatch MB40-006	Multibase, A Dow Corning Company	Siloxane, UHMW	Siloxane Masterbatch
Sinvicomp SSZ7209	Teknor Apex Asia Pacific PTE. LTD.	PVC, Flexible	Sinvicomp
APEX® 80328-Y FR	Teknor Apex Company	PVC, Flexible	APEX®
Durolon® V2700	Unigel Plásticos	PC	Durolon®
ESPRENE EPDM 5527F	Sumitomo Chemical Co., Ltd.	EPDM	ESPRENE EPDM

Category:	Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer:	UBE Engineering Plastics, S.A.
Trademark:	UBE Nylon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	xsoB5E_UBE-Nylon-5033-B.pdf