ALTECH® NXT PP-B A 2030/451 GF30 CP IM
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® NXT PP-B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xrvFfL_ALTECH-NXT-PP-B-A-2030-451-GF30-CP-IM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH® NXT PP-B A 2030/451 GF30 CP IM is a Polypropylene Copolymer (PP Copolymer) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Applications of ALTECH® NXT PP-B A 2030/451 GF30 CP IM include automotive and engineering/industrial parts. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Spiral Flow | |||
| 1.00 mm | 300 | mm | |
| 2.00 mm | 700 | mm |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 4500 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 15 | kJ/m² | |
| -40°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | 55 | kJ/m² | |
| -40°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 200 to 270 | °C | |
| Mold Temperature | 20.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C Z3510 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| YUNGSOX® PP 3504 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| Andur 7501 DP | Anderson Development Company | PUR-Ether/TDI | Andur |
| EnviroABS 530GF30 | West Michigan Compounding | ABS | EnviroABS |
| OP - PEI 40GF | Oxford Polymers | PEI | OP - PEI |