ULTEM™ foam DU319
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | ULTEM™ foam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xrmQ0c_ULTEM-foam-DU319.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact Compliant in recognized colors. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.29 | g/cm³ | ASTM D792 |
| -- | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (295°C/6.6 kg) | 8.1 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.17 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3370 | MPa | ASTM D638 |
| -- | 3300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 110 | MPa | ASTM D638 |
| Yield | 110 | MPa | ISO 527-2/5 |
| Break 3 | 82.0 | MPa | ASTM D638 |
| Break | 75.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 60 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/5 |
| Break 5 | 60 | % | ASTM D638 |
| Break | 36 | % | ISO 527-2/5 |
| Flexural Stress | |||
| -- | 155 | MPa | ISO 178 |
| Yield, 100 mm Span 6 | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 26 | J/m | ASTM D256 |
| -30°C 8 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 9 | 4.0 | kJ/m² | ISO 180/1A |
| Reverse Notch Izod Impact (3.20 mm) | 950 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 40.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 165 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 181 | °C | ASTM D1525 10 |
| -- | 177 | °C | ISO 306/B50 |
| -- | 180 | °C | ISO 306/B120 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 4.9E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 282 to 316 | °C | |
| Middle Temperature | 288 to 321 | °C | |
| Front Temperature | 293 to 327 | °C | |
| Nozzle Temperature | 299 to 332 | °C | |
| Processing (Melt) Temp | 299 to 332 | °C | |
| Mold Temperature | 93.3 to 149 | °C | |
| Back Pressure | 0.689 to 1.38 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 2.6 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bayflex® 190 RRIM (20% Mica) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| Cellophane™ 430MS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| DENILEN M 3539 | Vamp Tech | PP, Unspecified | DENILEN |
| EXCELLOY TK12G20 | Techno Polymer Co, Ltd. | ABS+PBT | EXCELLOY |
| LubriOne™ LB3100-8008 HS GR001 | PolyOne Corporation | PC+ABS | LubriOne™ |